Bulk Magnesium Diboride, Mechanical and Superconducting Properties
  Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low porosity) material with a sharp superconducting transition and critical current comparable with the best reported. Elastic constants were measured using method of resonant ultrasound spectroscopy. Their values for most dense samples (bulk modulus 142.5 GPa and Young's modulus 272.5 GPa) are close to theoretically predicted values for solid magnesium diboride. Porosity is resposible for lower values of elastic constants. Fracture toughness is evaluated based on measurements of microhardness and elastic constants. Upper critical field and irreversibility field are comparable with data for samples sintered at 3 GPa. Microstructural propeties of HIPed smaples are responsible for enhanced flux pinning. Method allows scaling of the size of the samples and manufacture of complex shapes. 
Vitali F. Nesterenko