Superconducting properties of MgB2 thin films prepared on flexible   plastic substrates
  Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in an Ar or vacuum atmosphere. In the optimal annealing process, the Mg-B films were heated to approximately 600 C, but at the same time, the backside of the structures was attached to a water-cooled radiator to avoid overheating of the plastic substrate. The resulting MgB2 films were amorphous with the onset of the superconducting transition at T_(c,on) about 33 K and the transition width of approximately 3 K. The critical current density was > 7x10^5 A/cm^2 at 4.2 K, and its temperature dependence indicated a granular film composition with a network of intergranular weak links. The films could be deposited on large-area foils (up to 400 cm^2) and, after processing, cut into any shapes (e.g., stripes) with scissors or bent multiple times, without any observed degradation of their superconducting properties. 
P. Kus, A. Plecenik, L. Satrapinsky, Y. Xu, and R. Sobolewski