High quality MgB2 thin films in-situ grown by dc magnetron sputtering
  Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained on both sapphire and MgO substrates. The best films showed maximum Tc = 35 K (onset), a transition width of 0.5 K, a residual resistivity ratio up to 1.6, a low temperature critical current density Jc > 1 MA/cm2 and anisotropic critical field with gamma = 2.5 close to the values obtained for single crystals. The preparation technique can be easily scaled to produce large area in-situ films. 
R. Vaglio, M. G. Maglione and R. Di Capua